One part, storage stable polymerization formulation

ABSTRACT

A one part, storage stable polymerizable formulation is provided that includes an ethenically unsaturated polymerizable compound intermixed with a free radical polymerization initiator and an organic solvent. The organic solvent provides storage stability and upon evaporation of the solvent, the rate of polymerization of the compound accelerates independent of addition of a second part. The formulation includes at least 30 total weight percent solids upon cure. Optional additives to the formulation include at least one of a cure accelerator, a filler, a plasticizer, a colorant, and a cure inhibitor. A process for forming a polymerized coating on an article involves the application of this formulation to the substrate of an article and allowing sufficient time for the solvent to evaporate to form the polymerized coating on the article. The substrate of the article forms a corrosion barrier even without prior removal of a native corrosion layer on a surface of the substrate of the article.

CROSS-REFERENCE TO RELATED APPLICATION

This application is a continuation of U.S. application Ser. No.12/898,436 filed Oct. 5, 2010 that in turn claims priority of U.S.Provisional Patent Application Ser. No. 61/248,636 filed Oct. 5, 2009,the contents of these applications are incorporated herein by reference.

FIELD OF THE INVENTION

The present invention in general relates to a one part polymerizableformulation well suited for coatings and in particular to free radicalinitiated polymerizable formulations that are stabilized in part throughsolvent dilution.

BACKGROUND OF THE INVENTION

The protection of a surface with a polymeric coating requires extensiveremoval of surface debris, grease, and other liquids from the surface,else the applied coating will have poor adhesion that reduces thecoating lifetime and exposes the substrate to environmental exposure.These difficulties are compounded when higher molecular weight polymerprecursors are used that, owing to size and conformational limitations,are unable to permeate well into a porous or scaly substrate. A furthercomplication of coating a surface with a polymerizable formulationentails mixing of a two part formulation to initiate the polymerizationreaction and coating formation. As a result, the formulation must beapplied on a timetable consistent with cure rate and also take intoaccount the ever-increasing viscosity of the formulation uponcombination of the formulation parts. The use of a two partpolymerizable formulation largely precludes spray application as curingtends to foul spray nozzles. Additionally, upon initiatingpolymerization of a two part formulation, any unused formulation iswasted.

Owing to these limitations, there exists a need for a one part, storagestable polymerizable formulation. Such a formulation is amenable tospray, roll or brush application.

SUMMARY OF THE INVENTION

A one part, storage stable polymerizable formulation is provided thatincludes an ethenically unsaturated polymerizable compound intermixedwith an optional free radical polymerization initiator and an organicsolvent. The organic solvent provides storage stability and uponevaporation of the solvent, the rate of polymerization of the compoundaccelerates independent of addition of a second part. The formulationincludes at least 30 total weight percent solids upon cure. Optionaladditives to the formulation include at least one of a cure accelerator,a filler, a plasticizer, a colorant, and a cure inhibitor. A process forforming a polymerized coating on an article involves the application ofthis formulation to the substrate of an article and allowing sufficienttime for the solvent to evaporate to form the polymerized coating on thearticle. The substrate of the article forms a corrosion barrier evenwithout prior removal of a native corrosion layer on a surface of thesubstrate of the article.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention has utility as a polymerizable formulation fromwhich a coating is formed upon application to a substrate. According tothe present invention, storage stability is obtained in a one partpolymerizable formulation through the inclusion of a quantity of solventsufficient to dilute an ethenically unsaturated polymerizable compoundand an initiator and/or catalyst to concentrations at which thepolymerization is arrested. As a result, consistent viscosityformulation is applied and only upon dissipation of the organic solventand exposure to air does polymerization of the inventive formulationkinetically accelerate. As a result, an inventive formulation is appliedwith a consistent viscosity and unused formulation is readily stored forfurther usage. Through selection of monomeric ethenically unsaturatedpolymerizable compounds, an inventive formulation is able to penetratethe surface of a fouled substrate prior to polymerization therebyallowing for protective coating to be applied to a substrate withlessened or no substrate preparation prior to application of theinventive formulation. Representative fouled substrates to which aninventive formulation are directly applied illustratively includecorroded metals such as rusted steel, oxidized aluminum, anodizedaluminum, pickled steel, stainless steel, painted metals, and hot dippedgalvanized steel, Galfan, Galvalume, Zincalume; cement; concrete; woodsubstrates such as painted wood, partially rotted wood, fabrics, drywalland plastics with porous surfaces as well as fiberboard. An inventiveformulation is particularly well suited for formulation as an aerosolwith a propellant. An attribute of a coating produced by an inventiveformulation is that an air and moisture barrier is formed that inhibitssubsequent corrosion of a substrate, even when already overlayered witha corrosion layer.

An ethenically unsaturated polymerizable compound operative in thepresent invention includes a carbon-carbon double bond referred tosynonymously herein as point of ethenic unsaturation. Operative moietiesfound within an inventive ethenically unsaturated polymerizable compoundinclude allylic moieties of the formula:

Y—X—(CR₂—RC═CR)_(n)—R  (I)

where R in each occurrence is independently H, C₁-C₄ alkyl, C₁-C₄perfluoroalkyl, C₆ aryl, C₆ aryl having at least one substituent ofC₁-C₄ alkyl; n is an integer of 1 to 50; and X is oxygen or R, Y is anullity or a polymeric resin backbone of acrylic, oligomeric ester of upto 30 repeat units, polyester, epoxy, polyether, alkyd, polyurethane. Itis appreciated that an oligomer or resin backbone may contain only asingle allylic moiety, two or multiple such moieties per structure (I)in the context of the present invention. In a preferred embodiment R ineach occurrence is H.

Acrylate moieties are also operative in an ethenically unsaturatedpolymerizable compound of an inventive formulation and have the generalformula:

Y—R—O(O)C—RC═CR₂  (II)

where R and Y are defined as above with respect to Formula (I).Methacrylate moieties of the formula YRO(O)C—CH₃C═CH₂ are particularlypreferred in an inventive formulation and noted to have a reducedreactivity relative to a corresponding purely protonated allylic andacrylate compound. As a general trend of reactivityallylic>acrylate>alkyl acrylate>aryl acrylate. Reactivity rates of agiven ethenically unsaturated polymerizable compound are a factor incontrolling storage stability of a formulation.

It is appreciated that inclusion of a mixture of compounds per structure(I) are readily prepared as an inventive formulation to optimize initialviscosity, storage stability, cure time, resultant coating hardness, andsubstrate adhesion characteristics. By way of example, an epoxy offormula (I) is noted to be well suited to improve adhesion to cleanmetal substrates such as aluminum and steel.

Representative ethenically unsaturated polymerizable compounds operativeherein illustratively include methyl methacrylate, hydroxyethylmethacrylate, tetrahydrofurfuryl methacrylate, trimethyl cyclohexylmethacrylate, cyclohexyl methacrylate, methacrylic acid, isobornylmethacrylate, ethoxyethyl methacrylate, 2-ethylhexyl methacrylate, anddicyclopentenyl oxyethyl methacrylate. Typical polyfunctional monomersinclude, but are not limited to, methacrylate esters of polyethyleneglycols, such as the esters of triethylene glycol 1,6-hexane dial,polypropylene glycol, 1,3- and 1,4-butylene glycol and1,12-dodecanediol, trimethylol propane trimethacrylate, ethoxylatedbisphenol A dimethacrylate.

Representative ethenically unsaturated materials may also include asuitable unsaturated alkyd. Alkyds are prepared from polyols, dibasicacids and fatty acid. They are essentially oil modified polyesters.Alkyds are classified into oxidizing or nonoxidizing types. Oxidizingalkyds cross-link through air oxidizing polymerization. Alkyds can befurther segmented into the amount of saturated or unsaturated oil thatis used. For example, alkyds with an oil length of greater than 60% arelong oil alkyds, oil lengths between 40 and 605 are known as medium oilalkyds and alkyds with less than 40% are known as short oil alkyds.Examples of unsaturated fatty acids for use to form alkyds that may becombined with suitable polyols and dibasic acids include soya, safflowerand sunflower. Alkyds that contain suitable unsaturated fatty aciddrying oils or other suitable ethenically unsaturated materials can beused in conjunction with other ethenically unsaturated compounds insubject invention.

Polymerization initiator is provided in an inventive formulation tocommence a free radical polymerization reaction so as to form covalentbonds between the ethenically unsaturated polymerizable compounds. Freeradical initiators operative herein illustratively include ketoneperoxide, diacyl peroxide, perester, perketals, diacyl peroxides,peroxydicarbonates, and hydroperoxide. Selection of a given initiatorfrom among those listed above is dependent on factors such as thedesired activation temperature of the inventive formulation, solubilityof the initiator inventive formulation through appreciation that solubleinitiators undergo homogeneous reaction catalysis that tends to befaster than that of insoluble initiators; and initiator degradationproducts. With respect to these factors, it is appreciated thatinitiator stability is dependent on energy activation associated withsteric hindrance and resonant structure stability. With respect toproducts of degradation, initiators typically degrade to reduced productless an abstracted oxygen atom. Stability of the substrate towards thisdegradation product represents a consideration in creation of aninventive formulation. By way of example, dibenzoyl peroxide generates aprimary degradation product of benzoic acid. Additionally, creating aninventive formulation, the inclusion of water within an organic solventdiluent is also a consideration as water typically reduces the effectivecure rate and is often less volatile than an organic solvent. By way ofan example, a free radical polymerization initiator having solubility inboth water and organic solvent tends to be more stable and thereforeless reactive in the presence of water. Representative initiatorsoperative herein illustratively include those organic hydroperoxideshaving the formula ROOH wherein R⁶ is a hydrocarbon radical containingup to about 18 carbon atoms, preferably an alkyl, aryl, or aralkylradical containing from one to 12 carbon atoms. Typical examples of suchhydroperoxides are cumene hydroperoxide, tertiary butyl hydroperoxide,methyl ethyl ketone peroxide, and hydroperoxides formed by theoxygenation of various hydrocarbons, such as methylbutene, cetane, andcyclohexene, and various ketones and ethers. Other examples of usefulinitiators include hydroperoxides such as p-methane hydroperoxide,2,5-dimethylhexane, and 2,5-dihydroperoxide. The initiator is typicallypresent from 1 to 6 weight percent of the polymerizable compound, withfrom 2 to 4 weight percent of the polymerizable compound beingpreferred.

An organic solvent is present in an inventive formulation as anonreactive diluent for the ethenically unsaturated polymerizablecompound and free radical initiator so as to impart storage stability tothe mixture of polymerizable compound and initiator. A suitable organicsolvent is nonreactive with the polymerizable compound and initiatorunder storage and polymerization conditions. Preferably, the organicsolvent is not a volatile organic compound (VOC) as defined by the U.S.Environmental Protection Agency. Suitable organic solvents operativeherein illustratively include methyl acetate, methyl ethyl ketone,toluene, tetrahydrofuran, aromatic 100, C₂-C₆ acetates such as n-propylacetate, t-butyl acetate, and n-hexyl acetate, and other ketone andester based oxygenated solvents. The organic solvent is selected so asto impart solubility on the polymerizable compound and preferably on thefree radical initiator as well. Preferably, an acetate constitutes amajority component of the organic solvent present. The organic solventis typically present from 1 to 40 weight percent of a fully formulatedinventive formulation. Organic solvent or mixture of solvents isselected not only to solubilize the polymerizable compound but also tovolatilize rapidly relative to the polymerization rate as residualsolvent can diminish the barrier properties of a coating formed from aninventive formulation. Preferably, the organic solvent is present from 1to 50 total weight percent. More preferably, the organic solvent issolely an acetate present from 5 to 40 total weight percent. In theevent that water is optionally added to the organic solvent, water istypically present from 1 to 10 total weight percent and preferably from2 to 8 total weight percent.

Optionally, a cure accelerator is provided to modify the kinetics andprogression of the polymerization process. Accelerators operative hereininclude salts of transition metals such as vanadium, molybdenum, cobalt,iron, zirconium, or copper. Of these transition metals, a combination ofcobalt and manganese is known to the art to promote surface curerelative to through cure while zirconium or a combination of cobalt andzirconium facilitates through cure. Cobalt accelerators, zirconiumaccelerators, and a combination thereof are known to induce oxidation.Suitable accelerator salts operative herein include naphthenates, acetylacetonates, and 2-ethyl hexanoic acid. Accelerators, if present, arefound in an inventive formulation in an amount from 0 to 10 total weightpercent and preferably between 0.01 and 1 total weight percent of thetransition metal salt itself.

In instances when an accelerator is present, an anti-skinning agent suchas an aliphatic keto oxime is provided to control surface oxidationassociated with transition metal accelerator. Other anti-skinning agentsare available as well as phenolics as well as nonphenolics and oximefree anti-skinning agents from suppliers such as OMG trade named Ascininmay also be used. Representative aliphatic keto oximes include methylethyl keto oxime, methyl propyl keto oxime, methyl terbutyl keto oxime,and methyl isobutyl keto oxime. Typically, an aliphatic keto oxime ispresent from 0.2 to 3.0 total weight percent and is preferably presentin concert with a cobalt-based accelerator. Cobalt-aliphatic keto oximecombinations are also known in the art to accelerate cure rates.

Other optional additives to an inventive formulation illustrativelyinclude fillers, plasticizers, colorants, and cure inhibitors.

Fillers operative in an inventive formulation illustratively includeparticulate of silica, glass microspheres, calcium carbonate, talc, micaclay, diatomaceous earth, glass microspheres, polymeric microspheres,and combinations thereof. A filler is typically present from 0 to 20total weight percent of a formulation. Fillers are appreciated to affectthe hardness of a resultant coating formed from an inventive formulationand modify the rheology of the formulation.

An optional plasticizer is provided to modify the hardness of aresultant coating formed from an inventive formulation. A plasticizer istypically present from 0 to 10 total weight percent and preferably from1 to 5 total weight percent. Plasticizers operative herein includephthalates such as diethyl, dibutyl, dibenzyl, and mixed benzyl-alkyl,and combinations thereof.

An optional colorant is provided to modify the hardness of a resultantcoating formed from an inventive formulation. A colorant is typicallypresent from 0 to 50 total weight percent and preferably from 2 to 25total weight percent. Colorants operative herein include organic,inorganic and mixed metal oxide pigments such as carbon black, titaniumoxide, phthalol blue, quinacridone red, red iron oxide, copper chromeblack, as well as soluble or insoluble dyes and combinations thereof.

An optional cure inhibitor is provided to modify the hardness of aresultant coating formed from an inventive formulation. A cure inhibitoris typically present from 0 to 5 total weight percent and preferablyfrom 0.1 to 3 total weight percent. Cure inhibitors operative hereininclude phthalates such as diethyl, dibutyl, dibenzyl, and mixedbenzyl-alkyl, and combinations thereof.

An inventive formulation is able to penetrate a corrosion overlayer andbond to an underlying substrate. Preferably, the cross-linking densityis such that an inventive coating forms an air and moisture barrier toinhibit subsequent corrosion. To achieve such a result, preferably aninventive formulation is greater than 30 total weight percent solids asmeasured by heat cured weight relative to the as-applied formulation.More preferably, the formulation is greater than 50 total weight percentsolids upon cure and most preferably is between 60 and 92 total weightpercent solids. It is appreciated that higher percent solidsformulations tend to have higher initial viscosities and higher coatingdensities relative to lower percent solids.

It is appreciated that only a thin coating of between 10 and about 500microns is needed to adequately protect a typical substrate. While aninventive formulation is readily applied to a substrate by swabbing orpump spray, it is appreciated that coating uniformity is readilyobtained by application from a spray aerosol, such as from a can. Assuch, a propellant is optionally added in a range from 5 to 95 totalweight percent with the proviso that the propellant and diluent solventtogether do not exceed 97 total weight percent of the formulation.Suitable propellants include those that are unreactive towards thecapped silanol fluid and illustratively include alkanes such as butane,pentane, isobutane, propane; ethers such as dimethyl ether, diethylether, nitrogen; halogenated hydrocarbons; carbon dioxide andcombinations thereof. The resultant formulation inclusive of apropellant is sealed within a conventional metal aerosol canister andapplied by spray application.

Upon complete cure, typically greater than 72 hours, an inventivecoating is amenable to reapplication of an inventive formulation or aconventional paint application. Suitable paints include oil-based,latex, and water-based paints.

The present invention is further detailed with respect to the followingnonlimiting examples.

Example 1

Thirty-five grams of trimethylol propane trimethacrylate are combinedwith 30 grams of 2 mol ethoxylated bisphenol A dimethacrylate and 20grams of polyallyl glycidyl ether diluted with 10 grams of toluene. Onegram of methacryloxypropyl trimethoxysilane is added along with 60milligrams of cobalt 2-ethyl hexanate and 60 milligrams of zirconium2-ethyl hexanate. Three grams of cumene hydroperoxide are added to thesolvent diluted ethenically unsaturated compound mixture. One gram ofmethyl ethyl keto oxime is mixed into the inventive formulation. Theinventive formulation is storage stable for more than 1 month at ambienttemperature fluctuating between 10° and 28° Celsius. The resultantformulation readily penetrates a rusted steel object and forms a coatingupon cure. A peel test on the cured coating performed at 20° Celsiusattached the rust layer and exposed clean steel substrate.

Example 2

The formulation of Example 1 is repeated with an allyl functionalaliphatic urethane replacing the ethoxylated bisphenol A methacrylateand t-butyl peroxy benzoate replacing cumene hydroperoxide at equivalentweight levels. The resultant formulation cured upon toluenevolatilization on a corroded steel substrate to achieve a comparablecoating.

Example 3

The formulation of Example 1 is repeated with toluene being replacedwith 6 grains of methyl acetate and 4 grams of methyl ethyl ketone. Acomparable coating is obtained upon dissipation of the methyl ethylketone and methyl acetate solvents on a rusted steel substrate.

Example 4

The formulation of Example 1 is repeated increasing the quantity oftrimethylol propane trimethacrylate to 50 grams with a decrease in theamount of ethoxylated bisphenol A dimethacrylate to 22 grams. Acomparison of formulation properties between Example 1 and Example 4 24hours after formulation in a sealed container at 20° Celsius, 2 hoursafter application to a wood substrate at 600 Celsius, and on wood after24 hours exposed to the environment at 20° Celsius is provided.

TABLE 1 Comparative Formulation Properties 24 h @ 20° C. 2 h @ 60° C. 24h @ 20° C. Formulation (sealed) (wood) (wood) Example 1 liquid hardcured Example 4 Gel hard cured

Example 5

The formulation of Example 1 is repeated with toluene being replacedwith 24.5 grams of t-butyl acetate and the inclusion of 2.4 grams ofcarbon black. The resultant formulation is storage stable for more than1 month at an ambient temperature fluctuating between 10° and 28°Celsius. The resultant formulation has a density of 1.03 kilograms perliter.

Example 6

Twelve grams of trimethylol propane trimethacrylate are combined with 31grams of a long oil soya alkyd, and 10 grams of 2 mol ethoxylatedbisphenol A dimethacrylate and 6 grams of polyallyl glycidyl etherdiluted with 16 grams of t-butyl acetate. 0.6 gram of methacryloxypropyltrimethoxysilane is added along with 51 milligrams of cobalt 2-ethylhexanate and 81 milligrams of zirconium 2-ethyl hexanate. 13 milligramsgrams of methyl ethyl ketoxime are added to the solvent dilutedethenically unsaturated compound mixture. 7 grams of a carbon blackpigment dispersion containing about 30% pigment is then added to themixture. The inventive formulation is storage stable for more than 1month at ambient temperature at 25° Celsius as well as 7 days at 120°Fahrenheit. The resultant formulation readily penetrates a rusted steelobject and forms a coating upon cure. A peel test on the cured coatingperformed at 200 Celsius attached the rust layer and exposed clean steelsubstrate.

Example 7

The formulation of Example 6 is applied to cold rolled steel and iscured at 60° Celsius with complete cure at 16 hours. Temperature cure isnoted in between 16 and 24 hours with the resultant inventive coatingcovered steel coupons being subjected to various tests. For comparison,the same steel coupons are coated with a conventional corrosioninhibition coating commercially available from Eastwood Company(Pottstown, Pa.). The Eastwood rust prevention solution is noted to dryin less than 8 hours to a comparable level of surface hardness and to becompletely tack and fingerprint free. The test coupons were subjected tothe following tests on separate coupons to determine coating attributes:

-   -   tensile hardness of cured film 72 hours after application via        ASTM D3363    -   methyl ethyl ketone (MEK) double rub solvent resistance rub test        per ASTM D4752    -   cyclic corrosion test per ASTM D6899 for 30 days through cycles        of moisture, salt, and acid rain    -   high humidity and temperature test 150 hours at 100% condensing        humidity at 49° Celsius for 150 hours    -   repeat of high humidity and temperature test for formulations        applied on pre-rusted steel        A summary of the environmental coating testing is provided below        in Table 2

TABLE 2 Summary of Environmental Coating Testing: Inventive Coating(Example 5) and Comparative Coating Example 6 Comparative PencilHardness* H 3B MEK Double Rub >100 3 Cyclic Corrosion naked eye rust,loss of visually unchanged adhesion, blistering High Humidity/ naked eyetarnish, rust High Temperature visually unchanged Pre-rusted HighHumidity/ naked eye rust, loss of High Temperature visually unchangedadhesion, blistering *Pencil hardness hardest to softest: 6H > 5H > 4H >3H > 2H > H > F > HB > B > 2E > 3B

Patent documents and publications mentioned in the specification areindicative of the levels of those skilled in the art to which theinvention pertains. These documents and publications are incorporatedherein by reference to the same extent as if each individual document orpublication was specifically and individually incorporated herein byreference.

The foregoing description is illustrative of particular embodiments ofthe invention, but is not meant to be a limitation upon the practicethereof. The following claims, including all equivalents thereof, areintended to define the scope of the invention.

1. A one part, storage stable polymerizable formulation comprising: afirst polymerizable compound comprising allylic moieties; a secondpolymerizable compound that has the formula:Y—X—(CR₂—RC═CR)_(n)—R  (1) where R in each occurrence is independentlyH, C₁-C₄ alkyl, C₁-C₄ perfluoroalkyl, C₆ aryl, C₆ aryl having at leastone substituent of C₁-C₄ alkyl; n is an integer of 1 to 50; X is oxygenor R; and Y is one of a nullity or a polymeric resin backbone ofacrylic, oligomeric ester of up to 30 repeat units, polyester, epoxy,polyether, alkyd, or polyurethane; an organic solvent in which saidpolymerizable compound and said second polymerizable compound aresoluble, said solvent providing storage stability and upon evaporationof said solvent, a rate of polymerization of said compound acceleratesindependent of addition of a second part; an anti-skinning agent; and atransition metal salt cure accelerator; and an optional additive of atleast one of a free radical polymerization initiator, a filler, aplasticizer, a colorant, and a cure inhibitor; wherein the formulationis at least 30 to 92 total weight percent solids.
 2. The formulation ofclaim 1 wherein the alkyd comprises an unsaturated fatty acid.
 3. Theformulation of claim 1 further comprising one or more monomericethylenically unsaturated polymerizable compounds of methacrylate estersof polyethylene glycols, trimethylol propane trimethacrylate, orethoxylated bisphenol A dimethacrylate.
 4. The formulation of claim 1further comprising a third polymerizable compound that has the formula:Y—R—O(O)C—RC═CR₂  (II) where R in each occurrence is independently H,C₁-C₄ alkyl, C₁-C₄ perfluoroalkyl, C₆ aryl, C₆ aryl having at least onesubstituent of C₁-C₄ alkyl and Y is an alkyd (II).
 5. The formulation ofclaim 4 wherein the alkyd (II) comprises an unsaturated fatty acid 6.The formulation of claim 1 further comprising water.
 7. The formulationof claim 1 wherein said solvent is at least one of: a methyl acetate,methyl ethyl ketone, toluene, tetrahydrofuran, C₂-C₆ alkyl acetate,AROMATIC 100, or AROMATIC
 150. 8. The formulation of claim 1 wherein theformulation is between 60 and 92 total weight percent solids.
 8. Theformulation of claim 1 wherein the transition metal cure accelerator ispresent.
 9. A one part, storage stable polymerizable formulationconsisting essentially of: a polymerizable compound that has theformula:Y—X—(CR₂—RC═CR)—R  (1) where R in each occurrence is independently H,C₁-C₄ alkyl, C₁-C₄ perfluoroalkyl, C₆ aryl, C₆ aryl having at least onesubstituent of C₁-C₄ alkyl; n is an integer of 1 to 50; X is oxygen orR; and Y is an alkyd; a free radical polymerization initiator; ananti-skinning agent; an organic solvent in which said polymerizablecompound and said second polymerizable compound are soluble, saidsolvent providing storage stability and upon evaporation of saidsolvent, a rate of polymerization of said compound acceleratesindependent of addition of a second part; and an optional additive of atleast one of a water, transition metal cure accelerator, a filler, aplasticizer, a colorant, and a cure inhibitor; wherein the formulationis at least 30 total weight percent solids.
 10. The formulation of claim9 wherein the alkyd comprises an unsaturated fatty acid drying oil. 11.The formulation of claim 9 wherein the transition metal cure acceleratoris present.
 12. The formulation of claim 9 wherein the water is present.13. The formulation of claim 9 wherein said solvent is at least one of:a methyl acetate, methyl ethyl ketone, toluene, tetrahydrofuran, C₂-C₆alkyl acetate, AROMATIC100, or AROMATIC
 150. 14. The formulation ofclaim 9 wherein the formulation is between 60 and 92 total weightpercent solids.
 15. A process of forming a polymerized coating on anarticle comprising: applying a formulation according to claim 1 to asubstrate of the article; and allowing sufficient time for said solventto evaporate to accelerate a rate of cure of said polymerizable compoundto form a polymerized coating on the article.
 16. The process of claim15 wherein the formulation is applied by one of spray, brush or roll.17. The process of claim 15 wherein the substrate is overlayered with acorrosion layer and the applying step occurs absent prior corrosionlayer removal and the formulation penetrates beneath the corrosion layerbefore cure and at least partially embeds the corrosion layer in thepolymerized coating.
 18. The process of claim 15 wherein the polymerizedcoating forms a moisture and air barrier.
 19. The process of claim 15further comprising adding a dye or pigment to the formulation prior tothe applying step.